Milled carbon fiber for plastic reinforcement

Milled carbon fiber for plastic reinforcement-Mechanism of Action of Carbon Fiber Powder Reinforced Plastics

Mechanical Reinforcement Mechanism

Load Transfer: After uniform dispersion, carbon fiber powder acts as a "rigid skeleton" to bear external loads and reduce the deformation of the plastic matrix. When the addition amount is 10%-20%, the tensile strength of the composite material can be increased by 50%-150%, and the flexural modulus can be increased by 100%-300%.
Inhibition of Crack Propagation: The high tear resistance of carbon fiber powder can block the spread of cracks in the plastic matrix and improve the impact resistance (for example, after adding 15% carbon fiber powder to PA6, the notched impact strength is increased by about 30%).

Improvement of Thermal Properties

The thermal expansion coefficient of carbon fiber powder (1-2×10⁻⁶/℃) is much lower than that of plastics (for example, the thermal expansion coefficient of PP is 100×10⁻⁶/℃), which can significantly reduce the thermal deformation rate of the composite material and increase the heat distortion temperature (HDT). For example, after adding 20% carbon fiber powder to POM, the HDT increases from 170℃ to above 220℃.

Enhancement of Functionality

Conductivity and Antistatic Property: The addition of carbon fiber powder reduces the volume resistivity of insulating plastics (such as PE) from 10¹⁶Ω・cm to 10²-10⁶Ω・cm, meeting the antistatic requirements of electronic equipment.

Optimization of Wear Resistance: The rigid particle filling effect of carbon fiber powder reduces the wear on the friction surface, and the wear rate can be reduced by 50%-80% (for example, the wear rate of PA+15% CF is only 1/5 of that of pure PA).

Adaptation Schemes of Typical Plastic Matrices and Carbon Fiber Powder

Engineering Plastics: PA (Nylon)

Application Scenarios: Automotive gears, bearing cages, high-pressure valve components.
Formula Design: Adding 10%-30% carbon fiber powder (particle size 5-15μm, surface amination treatment) can increase the tensile strength of PA6 from 75MPa to over 120MPa, while reducing water absorption (to minimize dimensional changes).

Special Engineering Plastics: PEEK

Application Scenarios: Aerospace structural parts, medical implants, high-temperature bearings.
Technical Points: The melting temperature of PEEK (343℃) is close to the oxidation temperature of carbon fibers. It is necessary to use carbon fiber powder with an anti-oxidation coating (such as nickel-plated or silicon-plated). When the addition amount is controlled at 15%-25%, the flexural modulus of PEEK can be increased from 3.8GPa to over 8GPa.

General Plastics: PP (Polypropylene)

Application Scenarios: Automotive bumpers, electronic device housings (with antistatic requirements).
<span style="-we

Reviews

There are no reviews yet.

Be the first to review “Milled carbon fiber for plastic reinforcement” Cancel reply
Your email address will not be published. Required fields are marked *
Your rating *
Your review *
Name *

Email *

Save my name, email, and website in this browser for the next time I comment.

Milled carbon fiber for plastic reinforcement

Mechanical Reinforcement Mechanism

Improvement of Thermal Properties

Enhancement of Functionality

Engineering Plastics: PA (Nylon)

Special Engineering Plastics: PEEK

General Plastics: PP (Polypropylene)

Reviews

Related products

Polypropylene chopped strands for dry mix

NR/SBR Rubber Sheet (HDM001)

Pickup Bucket

Oil-Resistant Rubber Gaskets – CNC Laser Cut Seals